GC Gold Label 2 LC / Fuji II LC (Powder-Liquid) Restorative GIC - Mini Pack A2

Light-Cured Reinforced Glass Ionomer Restorative - Resin reinforcement and light curing enhances physical and aesthetic properties making Gold Label 2LC one of GC’s top-of-the-line glass ionomer restorative.

GC Fuji II LC is the world-wide leading light-cured glass ionomer cement. Although designed primarily as a restorative material for use in Class III, V and deciduous teeth, GC Fuji II LC is a multipurpose material, with secondary indications such as liner, base and core build-up.

Key Features-

A Strontium-based Glass Ionomer:

All GC Gold Label Glass Ionomer contains strontium glass. The strontium glass provides good radiopacity and snapset characteristics, unanimously preferred by clinicians around the world. Interestingly, strontium will mimic calcium in the formation of strontium hydroxyapatite and strontium fluoroapatite to affect internal remineralization within the tooth structure.

Surface Strengthening Effect:

Research has shown that a strontium-based glass ionomer placed in calcium-containing environment (saliva) will result in calcium ion diffusing into the glass ionomer surface achieving a surface strengthening effect. All GC Gold Label Glass Ionomer strengthens over time in saliva.

A Consistent Predictable Seal:

All GC Gold Label Glass Ionomer will display a glossy surface after mixing. This indicates sufficient free polyacrylic acid is available to begin the ion exchange process. The subsequent movement of ions between dentin, enamel and GC Glass Ionomer creates an ion exchange zone which chemically fuses them together. The resulting seal is consistent, predictable and long lasting.

INDICATIONS

Class III and V restorations, particularly for cervical erosions and root surface caries

Restoration of primary teeth

Core build up

Cases where radiopacity is required

Geriatric applications

As a base or liner.

Powder / Liquid Ratio (g/g):3.2 / 1.0
Mixing Time (sec.):20-25 secs
Working Time (min., sec.): 3 mins45 secs
Light Curing Time (sec.):20 secs
Depth of Cure (A2) (mm):1.8

1. POWDER AND LIQUID DISPENSING

a) Select shade based on Vita shade guide.  : Vita is a registered trademark of Vita Zahnfabrik, Bad Säckingen, Germany

b) The standard powder to liquid ratio is 3.2g / 1.0g. 1 level scoop of powder to 2 drops of liquid

c) For accurate dispensing of powder, tap the bottle gently. Do not shake or invert

d) Hold the liquid bottle vertically and squeeze gently

e) Close bottles immediately after use

2. MIXING

a) Fluff powder of bottle before dispensing

b) Place one scoop of powder and two drops of liquid on pad. Divide powder in half

c) Spread liquid out into a thin layer (about the size of a half dollar or 3 cm) with plastic spatula

d) Pull half of the powder onto liquid and mix with lapping strokes (like impression material) for 10 to 15 seconds

e) Pull in remaining powder and mix thoroughly to a glossy consistency. Do not exceed 20-25 second total mixing time

3. RESTORATIVE TECHNIQUE

a) Prepare tooth using standard techniques. Extensive mechanical retention is not necessary. For pulp capping use calcium hydroxide

b) Apply GC CAVITY CONDITIONER (10 seconds) or GC DENTIN CONDITIONER (20 seconds) to the bonding surfaces using a cotton pellet or sponge

c) Rinse thoroughly with water. Dry by blotting with a cotton pellet or gently blowing with an air syringe. DO NOT DESICCATE. Best results are obtained when prepared surfaces appear moist (glistening)

d) Mix the required amount of cement. Working time is 3 minutes 45 seconds from the start of mixing at 23°C (73.4°F). Higher temperatures will shorten working time

e) Transfer cement to the preparation using a syringe or suitable placement instrument. Avoid air bubbles

f) Form the contour and place a transparent matrix if required

g) Light cure for 20 seconds using a visible light curing device (470 nm wavelength). Place light source as closely as possible to the cement surface. Note : For cavities deeper than 1.8 mm, use a layering technique

4. FINISHING

Remove matrix and finish under water spray using standard techniques. Note : Apply a final coat of GC Fuji VARNISH (blow dry) or GC Fuji COAT LC (light cure for 10 sec.) or G-COAT PLUS (light cure for 20 sec.).